=== Tri-polar mixtures ===
Adding tin to this bipolar-system complicates the behaviour even further. Some tin enters into the eutectic. A mixture of 4% tin, 12% antimony, and 84% lead solidifies at 240&nbsp;°C.

Depending from the metals in excess, compared with the eutectic, crystals are formed, depleting the liquid, until the eutectic 4/12 mixture is formed once more.

The 12/20 alloy contains many mixed crystals of tin and antimony, these crystals constitute the hardness of the alloy and the resistance against wear.

Raising the content of antimony cannot be done without adding some tin too. Because the fluidity of the mixture will dramatically diminish when the temperature goes down somewhere in the channels of the machine. Nozzles can be blocked by antimony crystals.